These corrosion data are mainly based on results of general corrosion laboratory tests, carried out with pure chemicals and water solutions nearly saturated with air (the corrosion rate can be quite different if the solution is free from oxygen).

All concentrations are given in weight-% and the solvent is water if nothing else is shown. The corrosion data apply to annealed materials with normal microstructure and clean surfaces, throughout.

Acetic acid, CH3COOH + sodium chloride, NaCL
Conc. CH3COOH, %113477-10101025
Conc. NaCL, %154158.552626
Temp. °C7050BP70-BP7080BPBPBP
Grade or type of alloy:
Carbon steel2
13 Cr2
Alleima® 18020p
Alleima® 3R120ps0ps1ps1ps1ps
Alleima® 3R600ps0p0ps0ps0ps0ps0ps1ps1ps
18Cr13Ni3Mo 1)
17Cr14Ni4Mo 2)
Alleima® 2RK65 ('904L')0ps0p0ps0ps0ps0ps0ps1ps1ps
Sanicro® 2800000000p0p
254 SMO000000000
654 SMO000000000
SAF™ 23040000p0002
SAF™ 220500000001p
SAF™ 2507000000000
Titanium (CP Ti)000000000

1) ASTM 317L, e.g. Alleima® 3R64
2) EN 1.4439, e.g. Alleima® 3R68

Symbol clarification

These corrosion tables use a number of symbols, having the following meanings:

Symbol Description
0 Corrosion rate less than 0.1 mm/year. The material is corrosion proof.
1 Corrosion rate 0.1—1.0 mm/year. The material is not corrosion proof, but useful in certain cases.
2 Corrosion rate over 1.0 mm/year. Serious corrosion. The material is not usable.
p, P Risk (severe risk) of pitting and crevice corrosion.
c, C Risk (Severe risk) of crevice corrosion. Used when there is a risk of localised corrosion only if crevices are present. Under more severe conditions, when there is also a risk of pitting corrosion, the symbols p or P are used instead.
s, S Risk (Severe risk) of stress corrosion cracking.
ig Risk of intergranular corrosion.
BP Boiling solution.
ND No data. (Used only where there are no actual data to estimate the risk of localised corrosion instead of p or s).

Disclaimer: Laboratory tests are not strictly comparable with actual service conditions. Accordingly, Alleima makes no warranties, express or implied, and accept no liability, compensatory or consequential, for the performance of different materials in individual applications that may be based on the information provided in this publication.