Alleima® 2RK65 HV is a vacuum arc-remelted high-alloy austenitic stainless steel with very high cleanliness resulting in good polishability. The grade is also characterized by very good overall corrosion resistance and good weldability.
Standards
- ASTM: '904L'
- UNS: N08904
- EN Number: 1.4539
- EN Name: X1NiCrMoCu25-20-5
- W.Nr.: 1.4539
- DIN: X 1 NiCrMoCu 25 20 5
- SS: 2562
- AFNOR: Z1NCDU25-20-4
Chemical composition (nominal)
| C | Si | Mn | P | S | Cr | Ni | Mo | Cu |
|---|---|---|---|---|---|---|---|---|
| ≤0.020 | 0.5 | 1.8 | ≤0.025 | ≤0.015 | 20 | 25 | 4.5 | 1.5 |
Mechanical properties
At 20°C (68°F)
The following figures apply to material in the solution annealed condition.
| Proof strength Rp0.2a) MPa ksi min. min. |
Rp1.0a) MPa min. |
ksi min. |
Tensile strength
Rm MPa ksi |
Elong. Ab) A2" % % min. min. |
Hardness Vickers. approx. |
|---|---|---|---|---|---|
| 230 33 | 250 | 36 | 520-720 75-104 | 35c) 35 | 160 |
1 MPa = 1 N/mm2
a) Rp0.2 and Rp1.0 correspond to 0.2% offset and 1.0% offset yield strength, respectively.
b) Based on L0 = 5.65 ÖS0 where L0 is the original gauge length and S0 the original cross-section area.
Physical properties
Density: 8.0 g/cm3, 0.29 lb/in3
| Temperature, °C | W/(m °C) | Temperature, °F | Btu/(ft h °F) |
|---|---|---|---|
| 20 | 12 | 68 | 7 |
| 100 | 14 | 200 | 8 |
| 200 | 16 | 400 | 9 |
| 300 | 18 | 600 | 10.5 |
| 400 | 20 | 800 | 11.5 |
| 500 | 22 | 1000 | 13 |
| 600 | 23 | 1200 | 14 |
| 700 | 25 | 1300 | 14.5 |
| Temperature, °C | J/(kg °C) | Temperature, °F | Btu/(lb °F) |
|---|---|---|---|
| 20 | 460 | 68 | 0.11 |
| 100 | 485 | 200 | 0.12 |
| 200 | 515 | 400 | 0.12 |
| 300 | 545 | 600 | 0.13 |
| 400 | 570 | 800 | 0.14 |
| 500 | 590 | 1000 | 0.14 |
| 600 | 605 | 1200 | 0.15 |
| 700 | 615 | 1300 | 0.15 |
| Temperature, °C | Per °C | Temperature, °F | Per °F |
|---|---|---|---|
| 30-100 | 15.5 | 86-200 | 8.5 |
| 30-200 | 16 | 86-400 | 9 |
| 30-300 | 16.5 | 86-600 | 9 |
| 30-400 | 17 | 86-800 | 9.5 |
| 30-500 | 17 | 86-1000 | 9.5 |
| 30-600 | 17.5 | 86-1200 | 9.5 |
| 30-700 | 17.5 | 86-1300 | 10 |
| Temperature, °C | μΩm | Temperature, °F | μΩin. |
|---|---|---|---|
| 20 | 0.94 | 68 | 37.0 |
| 100 | 0.99 | 200 | 38.8 |
| 200 | 1.07 | 400 | 42.2 |
| 300 | 1.13 | 600 | 44.6 |
| 400 | 1.15 | 800 | 45.5 |
| 500 | 1.17 | 1000 | 45.8 |
| 600 | 1.15 | 1200 | 45.9 |
| 700 | 1.18 | 1300 | 46.5 |
| Temperature, °C | MPa | Temperature, °F | ksi |
|---|---|---|---|
| 20 | 195 | 68 | 28.5 |
| 100 | 190 | 200 | 27.5 |
| 200 | 182 | 400 | 26.5 |
| 300 | 174 | 600 | 25 |
| 400 | 166 | 800 | 24 |
| 500 | 158 | 1000 | 22.5 |
Disclaimer: Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Alleima materials.