Alleima® 5LR11 is an austenitic stainless chromium-nickel steel.
Standards
- ASTM: 304
- UNS: S30400
- EN Number: 1.4301
- SS: 2333
- AFNOR: Z6CN18-09
- BS: 304S31
Product standards
- EN 10088-3
- ASTM A-314
Suitable for production of flanges etc. acc. to ASTM A-182
Certificates
Status according to EN 10 204 3.1
Chemical composition (nominal) %
C | Si | Mn | P | S | Cr | Ni | Mo | Others |
---|---|---|---|---|---|---|---|---|
0.05 | 0.6 | 1.3 | ≤0.040 | ≤0.015 | 18.5 | 8.5 | - | - |
Forms of supply
Sizes and tolerances
Round-cornered square, as well as round billets, are produced in a wide range of sizes according to the following tables. Larger sizes offered on request.
Surface conditions
Square billets
Unground, spot ground or fully ground condition.
Round billets
Peel turned or black condition.
Size mm |
Tolerance mm |
Length m |
---|---|---|
80 | +/-2 | 4 - 6.3 |
100, 114, 126, 140, 150 | +/-3 | 4 - 6.3 |
160, 180, 195, 200 | +/-4 | 4 - 6.3 |
>200 - 350 | +/-5 | 3 - 5.3 |
Sizes and tolerances apply to the rolled/forged condition.
Size mm |
Tolerance mm |
Length m |
---|---|---|
75 - 200 (5 mm interval) | +/-1 | max 10 |
>200 - 450 | +/-3 | 3 - 8 |
Size mm |
Tolerance mm |
Length m |
---|---|---|
77 - 112 (5 mm interval) | +/-2 | max 10 |
124, 134 | +/-2 | max 10 |
127, 147, 157 | +/-2 | max 10 |
142, 152, 163 | +/-2 | max 10 |
168, 178, 188 | +/-2 | max 10 |
183, 193 | +/-2 | max 10 |
Other products
Hollow bar
Mechanical properties
For billets testing is performed on separately solution annealed and quenched test piece. The following figures apply on material in the solution annealed and quenched condition.
At 20°C (68°F)
Proof strength | Tensile strength | Elong. | Contr. | HB | |
---|---|---|---|---|---|
Rp0.2a) | Rp1.0a) | Rm | Ab) | Z | |
MPa | MPa | MPa | % | % | |
approx. | |||||
≥205 | ≥230 | 515-680 | ≥45 | ≥50 | 170 |
Proof strength | Tensile strength | Elong. | Contr. | HB | |
---|---|---|---|---|---|
Rp0.2a) | Rp1.0a) | Rm | Ab) | Z | |
MPa | MPa | MPa | % | % | |
approx. | |||||
≥29.5 | ≥33.5 | 74.5-98.5 | ≥45 | ≥50 | 170 |
1 MPa = 1 N/mm2
a) Rp0.2 and Rp1.0 corresponds to 0.2% offset and 1.0% offset yield strength, respectively.
b) Based on L0 = 5.65√S0 , where L0 is the original gauge length and S0the original cross-section area.
The impact energy (Charpy V) at 20°C (68°F) is min 100 J (74 ft-lb).
At high temperatures
Temperature | Proof strength | Tensile strength | |
---|---|---|---|
Rp.02 | Rp1.0 | Rm | |
°C | MPa | MPa | MPa |
min. | min. | min. | |
100 | 155 | 190 | 450 |
200 | 127 | 155 | 400 |
300 | 110 | 135 | 380 |
400 | 98 | 125 | 380 |
500 | 92 | 120 | 360 |
Temperature | Proof strength | Tensile strength | |
---|---|---|---|
Rp.02 | Rp1.0 | Rm | |
°F | ksi | ksi | ksi |
min. | min. | min. | |
200 | 23.1 | 28.1 | 66.1 |
400 | 18.3 | 22.4 | 57.9 |
600 | 15.7 | 19.3 | 55.1 |
800 | 14.0 | 17.9 | 54.3 |
1000 | 13.1 | 17.4 | 48.9 |
Disclaimer: Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Alleima materials.