Sanicro® 35 Tube and pipe, seamless

Datasheet updated

2022-05-10 07:45
(supersedes all previous editions)

Sanicro® 35 is an alloy combining the best features of a super austenitic stainless steel and a nickel alloy. The grade has excellent corrosion resistance, for service in sea-water applications and other highly corrosive environments.

The grade is characterized by:

  • Excellent resistance to pitting and crevice corrosion
  • Excellent resistance to stress corrosion cracking (SCC)
  • High resistance to general corrosion in acid and caustic environments
  • High resistance to erosion-corrosion
  • Very high mechanical strength
  • Good weldability using nickel alloy consumables


  • UNS: N08935
  • Compliance with NACE MR0175/ISO 15156-3:2015, (Petroleum, Petrochemical, and Natural Gas Industries - Materials for Use in H2S-Containing Environments in Oil and Gas Production - Part 3: Cracking-Resistant CRAs (Corrosion-Resistant Alloys) and Other Alloys) for type 4a and type 4c materials.
  • Compliance with ANSI/NACE MR0103/ISO 17495-1:2016, (Petroleum, petrochemical and natural gas industries-Metallic materials resistant to sulfide stress cracking in corrosive petroleum refining environments) for highly alloyed austenitic stainless steels and nickel alloys.

Product standards

  • Seamless tube and pipe: ASTM B163


  • ASME Code Case 2982. Boiler and Pressure Vessel Code, Section VIII, Division I and II.
  • Pre-approval for Particular Material Appraisal (PMA), TÜV file 1326W043219

Chemical composition (nominal)

Chemical composition (nominal) %
C Si Mn P S Cr Ni Mo Cu N
≤0.030 ≤0.5 0.8 ≤0.030 ≤0.020 27 35 6.5 0.2 0.3


Due to its extremely good pitting and crevice corrosion properties, Sanicro® 35 is particularly suitable for applications where seawater is used for cooling or heating. Sanicro® 35 also has a high resistance to general corrosion in acid environments, making it suitable for a variety of applications.

Corrosion resistance

General corrosion

Sanicro® 35 has good resistance to hydrochloric acid compared to stainless steels with a lower chromium and molybdenum content and can, therefore, be useful in environments where hydrochloric acid is present. See Figure 1.

Figure 1. Isocorrosion in hydrochloric acid. The curves represent a corrosion rate of 0.1 mm/year.

Sanicro® 35 has a high resistance to sulfuric acid and nitric acid. Isocorrosion diagrams can be seen in Figure 2 and Figure 3.

Figure 2. Isocorrosion in naturally aerated sulfuric acid. The curves represent a corrosion rate of 0.1 mm/year.

Figure 3. Isocorrosion in nitric acid. The curves represent a corrosion rate of 0.1 mm/year.

Sanicro® 35 also performs well in mixtures of formic acid and acetic acid, see Table 1.

Table 1. Corrosion rate of Sanicro 35 in mixtures of acetic acid (CH3COOH) and formic acid (HCOOH) at boiling conditions.

Concentration CH3COOH, % 50 50 50 50
Concentration HCOOH, % 10 15 20 25
Corrosion rate, mm/year 0.00 0.00 0.00 0.01

Sanicro® 35 performs well also in alkaline conditions showing high corrosion resistance in caustic solutions, see Table 2.

Table 2. Corrosion rate of Sanicro® 35 in sodium hydroxide (NaOH) at various concentrations and temperatures.

Concentration NaOH % 40 50 60 70
Temperature (°C) 120 120 120 130
Corrosion rate, mm/year 0.06 0.05 0.03 0.01

Pitting corrosion

One of the main advantages of Sanicro® 35 is that it has excellent resistance to pitting corrosion. The pitting resistance comes from the high contents of chromium, molybdenum, and nitrogen. The PREN-number can be used to compare and rank alloys with respect to the chemical composition and possibility to resist pitting. The PREN is defined as, in weight-%;

PREN = %Cr + 3.3 x %Mo +16 x %N

The nominal PREN value for Sanicro® 35 is ~52, comparable to the nickel alloy Sanicro® 625 (Alloy 625). This is significantly higher than e.g. the PREN values for super duplex and 6 Mo austenitic grades which are commonly used in seawater applications. For reference, SAF 2507 and Alleima 254 SMO have a minimum PREN-value of 42.5.

The critical pitting temperature (CPT) has been determined in 6% FeCl3 according to ASTM G48 practice C. The CPT has also been determined in a potentiostatic test in a 3M MgCl2 solution. The test was performed in a modified ASTM G150 test where the solution was changed from 1M NaCl to allow the CPT-measurement of highly alloyed materials. The measured CPT-values can be seen in Table 3.

Table 3. CPT-values for Sanicro® 35 compared to Alleima 254 SMO. The CPT was measured on coupons with P120 surface for the ASTM G48 test and P600 surface for the G150 mod. test.

Alloy CPT (°C)
Mod. G150 in 3M MgCl2 ASTM G48 method C
Sanicro® 35 110 >851)2)
Alleima 254 SMO 67 653)
Alloy C276 N/A >851)2)
Alloy 625 N/A >851)2)

1) According to the standard ASTM G48, the method was developed to be used up to 85°C.
2) Method C
3) Method E

Crevice corrosion

Crevice corrosion resistance is equally as important as pitting resistance since crevices can rarely be totally avoided. Sanicro® 35 has excellent crevice corrosion resistance in chloride environments. The critical crevice temperature (CCT) has been determined by potentiostatic tests in 1M NaCl according to standard ASTM G150 and by immersion tests in 6% FeCl3 test solution acidified with HCl according to ASTM G48, see Table 4.

Table 4. CCT-values for Sanicro® 35 compared to some alloys according to various test methods. The applied potential was 700 mV vs. SCE as per ASTM G150. Flat coupons were tested with surfaces wet ground with P600 grit paper for the ASTM G150 test and with P120 for the ASTM G48 tests.

Alloy CCT (°C)
ASTM G1501) ASTM G48
method D2)
method F3)
Sanicro® 35 100 52.5 45
Alloy C276 52.5 42.5
Alloy 625 45 25
Alleima 254 SMO 75 35

1) crevice formers according to ISO 18070 with applied momentum of 3 Nm
2) applied momentum of 0.28 Nm
3) applied momentum of 1.58 Nm

Testing in seawater

Accelerated laboratory tests are very good for ranking different alloys, however, real application environment tests are also valuable. Materials are often used in a seawater environment which is very corrosive for many alloys. Sanicro® 35 has been tested for 90 days in natural seawater at 30°C where a biofilm is active and also in 0.5 ppm chlorinated seawater at elevated temperatures.

Table 5. Flat specimens with surfaces ground with P120 grit paper tested in real seawater.

Test condition Pitting corrosion Crevice corrosion1)
30°C natural seawater No No

80°C chlorinated seawater (0.5 ppm residual Cl)

No N/A

1) crevice formers according to ISO 18070 with applied crevice pressure of 3 N/mm2

Stress corrosion cracking

Ordinary austenitic steels of the ASTM 316 type are susceptible to chloride-induced stress corrosion cracking (SCC) in chloride bearing solutions at temperatures above about 60°C (140°F). This susceptibility declines with increasing nickel content. Chromium contents above 20% can also be beneficial. Sanicro® 35 has excellent resistance to SCC. This is demonstrated in Table 6, which shows the results of SCC tests in a 40% calcium chloride solution. The grade showed no cracking or corrosion after 500 hours of constant load testing, corresponding to 90% of the actual ultimate tensile strength at 100°C. It should be noted that the high loading of 90% of UTS naturally causes plastic deformation of the specimens.

Table 6. Result of stress corrosion cracking test of different alloys in aerated 40% CaCl2, at 100°C (210°F), pH 6.5

Alloy % of UTS

Time to failure (h)

Sanicro® 35 90 >500 No attack
Sanicro® 28 90 >500 No attack
ASTM TP 316 90 <70 Pitting and cracking

Sanicro® 35 does not suffer from SCC in a NACE MR 0175 / ISO 15156 Test Level VI environment. Slow strain rate testing (SSRT) was performed on cold worked Sanicro® 35 material (140 ksi and 180 ksi), according to NACE TM0198. The environment had partial pressures of 500 psia H2S and 500 psi CO2. 20 wt-% sodium chloride was used as test solution and the temperature was 175°C ± 3°C. For both the 140 ksi and 180 ksi materials, two specimens were tested in the corrosive environment and one in nitrogen. All tests were carried out at the same baseline temperature. Both materials show ductile fractures with ratios of ≥92% for time to failure, elongation to failure, plastic strain to failure and reduction in area compared to inert environment, which indicates no SCC.

Hydrogen embrittlement

Sanciro® 35 shows as expected excellent resistant to hydrogen embrittlement since it has high austenitic phase stability. Sanciro® 35 is not a precipitation-hardened grade which the latter may experience hydrogen embrittlement.

Sanicro® 35 solution annealed material experienced no cracking in constant load testing at 4°C in 3% NaCl at -1050 mVSCE at two different loads present in Table 7. This indicates that the alloy is not prone to hydrogen embrittlement and is a viable option for subsea applications.

Table 7. Sanicro® 35 results from constant load testing at 4°C in 3% NaCl at -1050 mVSCE

Load/Yield strength, % Load, MPa Time to failure, h Cracking, Yes/No
100 427 >500 No
120 509 >500 No



The force needed for bending Sanicro® 35 is higher than that for standard austenitic stainless steels which is a natural consequence of the higher yield strength. The excellent formability of the grade permits cold bending to tight bending radii.


Sanicro® 35 can be expanded into tube sheets in the same way as standard austenitic stainless steels.

Forms of supply

Sanicro® 35 can be supplied as seamless tube and pipe.

Heat treatment

Tubes are delivered in solution annealed condition. If additional heat treatment is needed after further processing, please contact Alleima.

Mechanical properties

The following figures apply to material in the solution annealed condition.

At 20°C (68°F)

Metric units

Proof strength Tensile Strength Elongation
Rp0.2a Rm A2”
MPa MPa %
≥425 ≥750 ≥35

Imperial units

Proof strength Tensile Strength Elongation
Rp0.2a Rm A2”
ksi ksi %
≥62 ≥109 ≥35

1 MPa = 1 N/mm2
a) Rp0.2 and Rp1.0 corresponds to 0.2% and 1.0% offset yield strength.
b) Based on L0 = 5.65 √S0 where L0 is the original gauge length and S0 the original cross-section area.

At high temperatures

Intermetallic phases are precipitated at temperatures above 600°C (1110°F). Therefore, the steel should not be exposed to these temperatures for prolonged periods.

Metric units

Temperature Proof strength Tensile strength Elongation
Rp0.2 Rm A
°C MPa MPa %
Min. Min. Min.
100 350 680 35
200 300 620 35
300 275 600 35
400 250 580 35

Imperial units

Temperature Proof strength Tensile strength Elongation
Rp0.2 Rm A
°F ksi ksi %
Min. Min. Min.
200 51 98 35
400 43 90 35
600 39 87 35
800 36 84 35

Physical properties

Density: 8.1 g/cm3, 0.29 lb/in3

Thermal conductivity

Temperature, °C W/(m °C) Temperature, °F Btu/(ft h °F)
20 10.0 68 6.0
100 12.0 200 7.0
200 13.5 400 8.0
300 15.5 600 9.0
400 17.0 800 10.0

Specific heat capacity

Temperature, °C J/(kg °C) Temperature, °F Btu/(lb °F)
20 450 68 0.11
100 470 200 0.11
200 500 400 0.12
300 510 600 0.12
400 530 800 0.13

Thermal expansion

Metric units, x10-6/°C

Temperature, °C 30-100 30-200 30-300 30-400
Sanicro® 35 14.0 14.5 15.0 15.5
Carbon steel 12.5 13.0 13.5 14.0
ASTM 316L 16.5 17.0 17.5 18.0

Imperial units, x10-6/°F

Temperature, °C 86-200 86-400 86-600 86-800
Sanicro® 35 8.0 8.0 8.5 8.5
Carbon steel 7.0 7.0 7.5 8.0
ASTM 316L 9.5 9.5 10.0 10.0


Temperature, °C μΩm Temperature, °F μΩinch
20 1.0 68 39

Modulus of elasticity, x103

Temperature, °C MPa Temperature, °F ksi
20 190 68 28.0
100 185 200 27.0
200 180 400 26.0
300 175 600 25.0
400 170 800 24.5


The weldability of Sanicro® 35 is good and a suitable method for fusion welding is TIG welding (GTAW).

Welding should be undertaken with low heat input, maximum 1.2 kJ/mm, and interpass temperature 100 °C maximum. A stringer welding technique should be used. Preheating and post-weld heat treatment are not necessary. To maintain full corrosion resistance of the welded joint, welding must be followed by thorough cleaning to ensure the removal of all oxides and heat tint. Ar + 2 %N2 is recommended as shielding gas and backing gas with TIG welding to achieve the best combination of mechanical properties and corrosion resistance of the welded joints.

Welding of fully austenitic stainless steels and nickel-base alloys often involves the risk of hot cracking in the welded joints if the weldment is under constrain. Sanicro® 35, however, possesses very high purity, and is thereby less prone to hot cracking than most of the nickel-base alloys.

Nickel alloy UNS N06059 (ERNiCrMo-13, NiCr23Mo16) wire or rod is recommended as filler material for gas shielded arc welding. Welding without filler material is not recommended.

Disclaimer: Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Alleima materials.